Brick is one of the materials of building which have been long known and used by the people bothin rural area as well as urban area. Brick is a material made of clay with or without additionalmixture through several processes. The process includes of draining in the sun and then burning inhigh temperature in order to make the brick harden and not broken if it is soaked into the water. Inthis study used clay and additional materials ISS 2500 which has a variety of levels of 0.9 ml, 1.2ml, 1.5 ml and 1.8 ml with the purpose to improving the quality of the bricks, as well as tocompare compressive strength of bricks by modifying the length of the time combustion. So thatcan be known a long time the most optimal combustion.Soil samples were tested in this study are derived from clay Nyunyai Street, District Rajabasa,Bandar Lampung. Variations of burning time is used for one day, two days and three days. Beforebrick printed, the soil sample that has been mixed with the ISS 2500 and cured for 7 days, afterthat, the soil sample is printed, then drying for 2 weeks, along with treatment without burning andburning bricks. Based on the results of physical test of originil solid, USCS classified the sampleof solid as the clay with low plasticity.Based on the results of sample's physical, USCS classify soil sample as clay with low plasticity.Compressive strength test results of the four levels of post combustion, the compressive strengthmaximum average post-combustion bricks are at a level of 1.8 ml with a burning for two days.The compressive strength value of 31.86 kg/cm 2 . The compressive strength maximum averagebrick before combustion generated by the level of 1.8 ml in the amount of 7.79 kg /cm 2 .