Reaction Kinetic Analysis of Syntesized Lifepo4 Using Kissinger Method

Indra Gunawan
Journal article Indonesian Journal of Materials Science • February 2012

Download full text
(Bahasa Indonesia, 5 pages)

Abstract

The reaction kinetic analyses of synthesized LiFePO4 have been done using Kissinger method. LiFePO4 was prepared by mixing equimolar amount of LiCl, FeCl2.4H2O and H3PO4 in distilled water solution. Solution homogenization was achived by magnetic stirring and heating at 60 ºC. LiFePO4 precursor obtained after heat treatment at 200 ºC for 2 hours. LiFePO4 precursor was then analysized by using Differential Thermal Analysis (DTA) at heating rate of 5, 10, 15 and 20 ºC min-1 respectively. LiFePO4 powder was obtained after heating at 700 ºC for 4 hours, then the X-Ray Diffactometer (XRD) analysis was done to confirm phase purity and crystalline structure, meanwhile morphology observation was done by using Scanning Electron Microscope (SEM). By using Kissinger method, activation energy of LiFePO4 formation reaction was about Ea = 412 kJmol-1, and the frequeny factor A =1,1705 x 103.

Metrics

  • 172 views
  • 96 downloads

Journal

Indonesian Journal of Materials Science

Jurnal Sains Materi Indonesia (JUSAMI; Indonesian Journal of Materials Science) merupakan jurnal ... see more